Golf Ball Having Ionomer/Hydrophobic Thermoplastic Polyurethane Layers

ABSTRACT

A golf ball has moisture resistant layer comprising a blend of at least one ionomer and hydrophobic thermoplastic polyurethane. The moisture resistant layer may be part of the cover layer, for example an inner layer of a two-layer cover layer. The moisture resistant layer may be an intermediate layer between the core and the cover.

This application claims benefit from U.S. Provisional application No.61/312,286, filed Mar. 10, 2010, the whole contents of which areincorporated herein by reference in its entirety.

FIELD OF THE INVENTION

The present invention relates to golf balls. Particular example aspectsof this invention relate to golf balls having materials that improve themoisture resistance of the ball as well as scruff resistance, softness,and flexibility of the golf ball layers.

BACKGROUND

Golf is enjoyed by a wide variety of players—players of differentgenders and dramatically different ages and/or skill levels. Golf isunique in the sporting world in that such diverse collections of playerscan play together in golf events, even in direct competition with oneanother (e.g., using handicapped scoring, different tee boxes, in teamformats, etc.), and still enjoy the golf outing or competition. Thesefactors, together with the increased availability of golf programming ontelevision (e.g., golf tournaments, golf news, golf history, and/orother golf programming) and the rise of well known golf superstars, atleast in part, have increased golf's popularity in recent years, both inthe United States and across the world.

Golfers at all skill levels seek to improve their performance, lowertheir golf scores, and reach that next performance “level.”Manufacturers of all types of golf equipment have responded to thesedemands, and in recent years, the industry has witnessed dramaticchanges and improvements in golf equipment. For example, a wide range ofdifferent golf ball models now are available, with balls designed tocomplement specific swing speeds and/or other player characteristics orpreferences, e.g., with some balls designed to fly farther and/orstraighter; some designed to provide higher or flatter trajectories;some designed to provide more spin, control, and/or feel (particularlyaround the greens); some designed for faster or slower swing speeds;etc. A host of swing and/or teaching aids also are available on themarket that promise to help lower one's golf scores.

Being the sole instrument that sets a golf ball in motion during play,golf clubs also have been the subject of much technological research andadvancement in recent years. For example, the market has seen dramaticchanges and improvements in putter designs, golf club head designs,shafts, and grips in recent years. Additionally, other technologicaladvancements have been made in an effort to better match the variouselements and/or characteristics of the golf club and characteristics ofa golf ball to a particular user's swing features or characteristics(e.g., club fitting technology, ball launch angle measurementtechnology, ball spin rate measurement technology, ball fittingtechnology, etc.).

Modern golf balls generally comprise either a one-piece construction orseveral layers including an outer cover surrounding a core. Some golfball layers include thermoplastic urethane (TPU) type materials. Aproblem experienced with thermoplastic urethane type layer materials ishigh Water Vapor Transmission Rate (WVTR.) The problem arises whenmoisture penetrates the ball over time and will harden the ball's rubbercore, or any other rubber layer. This will change the ball's performanceand durability.

While the industry has witnessed dramatic changes and improvements togolf equipment in recent years, some players continue to look forincreased distance on their golf shots, particularly on their drives orlong iron shots, and/or improved spin or control of their shots,particularly around the greens. Accordingly, there is room in the artfor further advances in golf technology.

SUMMARY

The following presents a general summary of aspects of the disclosure inorder to provide a basic understanding of the disclosure and variousaspects of it. This summary is not intended to limit the scope of thedisclosure in any way, but it simply provides a general overview andcontext for the more detailed description that follows.

Aspects of this invention are directed to a golf ball having at leastone layer comprising a blend of at least one ionomer and hydrophobicthermoplastic polyurethane. The at least one layer may be a core layer,a cover layer, or any intermediate layer.

Other aspects of this invention are directed to methods for making agolf ball having at least one layer applying a coating comprising atleast one ionomer and hydrophobic thermoplastic polyurethane.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete understanding of the present invention and certainadvantages thereof may be acquired by referring to the followingdetailed description in consideration with the accompanying drawings, inwhich:

FIG. 1 schematically illustrates a golf ball having dimples.

FIG. 2 schematically illustrates a cross-sectional view of a golf ballin accordance with FIG. 1.

FIG. 3 schematically illustrates another cross-sectional view of a golfball in accordance with FIG. 1.

FIG. 4 provides Moisture Vapor Transmission Rates for variousHydrophobic TPU blends.

The reader is advised that the various parts shown in these drawings arenot necessarily drawn to scale.

DETAILED DESCRIPTION

In the following description of various example structures, reference ismade to the accompanying drawings, which form a part hereof, and inwhich are shown by way of illustration various example golf ballstructures. When the same reference number appears in more than onedrawing, that reference number is used consistently in thisspecification and the drawings to refer to the same or similar partsthroughout. Additionally, it is to be understood that other specificarrangements of parts and structures may be utilized and structural andfunctional modifications may be made without departing from the scope ofthe present invention. Also, while terms such as “top,” “bottom,”“front,” “back,” “rear,” “side,” “underside,” “overhead,” and the likemay be used in this specification to describe various example featuresand elements of the invention, these terms are used herein as a matterof convenience, e.g., based on the example orientations shown in thefigures and/or the orientations in typical use. Nothing in thisspecification should be construed as requiring a specific threedimensional or spatial orientation of structures.

A. General Description of Golf Balls and Manufacturing Systems andMethods

Golf balls may be of varied construction, e.g., one-piece balls,two-piece balls, three-piece balls (including wound balls), four-pieceballs, five-piece balls, etc. The difference in play characteristicsresulting from these different types of constructions can be quitesignificant. Generally, golf balls may be classified as solid or woundballs. Solid balls that have a two-piece construction, typically across-linked rubber core, e.g., polybutadiene cross-linked with zincdiacrylate and/or similar cross-linking agents, encased by a blendedcover, e.g., ionomer resins, are popular with many average recreationalgolfers. The combination of the core and cover materials provide arelatively “hard” ball that is virtually indestructible by golfers andone that imparts a high initial velocity to the ball, resulting inimproved distance. Because the materials from which the ball is formedare very rigid, two-piece balls tend to have a hard “feel” when struckwith a club. Likewise, due to their hardness, these balls have arelatively low spin rate, which also helps provide greater distance.

Wound balls are generally constructed from a liquid or solid centersurrounded by tensioned elastomeric material and covered with a durablecover material, e.g., ionomer resin, or a softer cover material, e.g.,balata or polyurethane. Wound balls are generally thought of asperformance golf balls and have good resiliency, desirable spincharacteristics, and good “feel” when struck by a golf club. However,wound balls are generally difficult to manufacture as compared to solidgolf balls.

More recently, three- and four-piece balls have gained popularity, bothas balls for average recreational golfers as well as performance ballsfor professional and other elite level players. Such balls typicallyinclude a core (optionally a multi-part core, such as an inner core andan outer core), one or more mantle or intermediate layers (also called“inner cover” layers), and an outer cover layer.

A variety of golf balls have been designed to provide particular playingcharacteristics. These characteristics generally include the initialvelocity and spin of the golf ball, which can be optimized for varioustypes of players. For instance, certain players prefer a ball that has ahigh spin rate in order to control and stop the golf ball around thegreens. Other players prefer a ball that has a low spin rate and highresiliency to maximize distance. Generally, a golf ball having a hardcore and a soft cover will have a high spin rate. Conversely, a golfball having a hard cover and a soft core will have a low spin rate. Golfballs having a hard core and a hard cover generally have very highresiliency for distance, but they may “feel” hard and be difficult tocontrol around the greens.

The carry distance of some conventional two-piece balls has beenimproved by altering the typical single layer core and single coverlayer construction to provide a multi-layer ball, e.g., a dual coverlayer, dual core layer, and/or a ball having an intermediate layerdisposed between the cover and the core. Three- and four-piece balls arenow commonly found and commercially available. Aspects of this inventionmay be applied to all types of ball constructions, including the wound,solid, and/or multi-layer ball constructions described above.

FIG. 1 is a perspective view of a solid golf ball 100 according to anaspect of the invention. Golf ball 100 may be generally spherical inshape with a plurality of dimples 102 arranged on the outer surface 108of golf ball 100 in a pattern 112.

Internally, golf ball 100 may be generally constructed as a multilayersolid golf ball, having any desired number of pieces. In other words,multiple layers of material may be fused, blended, or compressedtogether to form the ball. The physical characteristics of a golf ballmay be determined by the combined properties of the core layer(s), anyoptional mantle layers, and the cover. The physical characteristics ofeach of these components may be determined by their respective chemicalcompositions. The majority of components in golf balls compriseoligomers or polymers. The physical properties of oligomers and polymersmay be highly dependent on their composition, including the monomerunits included, molecular weight, degree of cross-linking, etc. Examplesof such properties may include solubility, viscosity, specific gravity(SG), elasticity, hardness (e.g., as measured as Shore D hardness),rebound resilience, scuff resistance, etc. The physical properties ofthe oligomers and polymers used may also affect the industrial processesused to make the components of the golf ball. For example, whereinjection molding is the processing method used, extremely viscousmaterials may slow down the process and thus viscosity may become alimiting step of production.

As shown in FIG. 2, one aspect of such a golf ball (referred togenerally as 200) includes a core 204, a cover 208, and an intermediatelayer 206 between core 204 and cover 208. Cover 208 surrounds, encloses,encompasses, etc., the core and any other internal layers of the ball.Cover 208 has an outer surface that may include a dimple patterncomprising a plurality of dimples.

As shown in FIG. 3, another aspect of such a golf ball (referred togenerally as 300) includes a core 304, a cover 308, and intermediatelayers 306 and 310 between core 304 and cover 308. Cover 308 surrounds,encloses, encompasses, etc., the core and any other internal layers ofthe ball. Cover 308 has an outer surface that may include a dimplepattern comprising a plurality of dimples.

The Center

A golf ball may be formed, for example, with a center having a lowcompression, but still exhibit a finished ball COR and initial velocityapproaching that of conventional two-piece distance balls. The centermay have, for example, a compression of about 60 or less. The finishedballs made with such centers have a COR, measured at an inbound speed of125 ft./s., of about 0.795 to about 0.815. “COR” refers to Coefficientof Restitution, which is obtained by dividing a ball's rebound velocityby its initial (i.e., incoming) velocity. This test is performed byfiring the samples out of an air cannon at a vertical steel plate over arange of test velocities (e.g., from 75 to 150 ft/s). A golf ball havinga high COR dissipates a smaller fraction of its total energy whencolliding with the plate and rebounding therefrom than does a ball witha lower COR.

The terms “points” and “compression points” refer to the compressionscale or the compression scale based on the ATTI Engineering CompressionTester. This scale, which is well known to persons skilled in the art,is used in determining the relative compression of a center or ball.

The center may have, for example, a Shore C hardness of about 40 toabout 80. The center may have a diameter of about 0.75 inches to about1.68 inches. The base composition for forming the center may include,for example, polybutadiene and about 20 to 50 parts of a metal saltdiacrylate, dimethacrylate, or monomethacrylate. If desired, thepolybutadiene can also be mixed with other elastomers known in the art,such as natural rubber, styrene butadiene, and/or isoprene, in order tofurther modify the properties of the center. When a mixture ofelastomers is used, the amounts of other constituents in the centercomposition are usually based on 100 parts by weight of the totalelastomer mixture. In other examples, the center (or core) may be madefrom resin materials, such as HPF resins (optionally with barium sulfateincluded therein), which are commercially available from E.I. DuPont deNemours and Company of Wilmington, Del.

Metal salt diacrylates, dimethacrylates, and monomethacrylates includewithout limitation those wherein the metal is magnesium, calcium, zinc,aluminum, sodium, lithium or nickel. Zinc diacrylate, for example,provides golf balls with a high initial velocity in the United StatesGolf Association (“USGA”) test.

Free radical initiators often are used to promote cross-linking of themetal salt diacrylate, dimethacrylate, or monomethacrylate and thepolybutadiene. Suitable free radical initiators include, but are notlimited to peroxide compounds, such as dicumyl peroxide;1,1-di(t-butylperoxy) 3,3,5-trimethyl cyclohexane;bis(t-butylperoxy)diisopropylbenzene; 2,5-dimethyl-2,5di(t-butylperoxy)hexane; or di-t-butyl peroxide; and mixtures thereof.The initiator(s) at 100 percent activity may be added in an amountranging from about 0.05 to about 2.5 pph based upon 100 parts ofbutadiene, or butadiene mixed with one or more other elastomers. Oftenthe amount of initiator added ranges from about 0.15 to about 2 pph, andmore often from about 0.25 to about 1.5 pph. The golf ball centers mayincorporate 5 to 50 pph of zinc oxide (ZnO) in a zincdiacrylate-peroxide cure system that cross-links polybutadiene duringthe core molding process.

The center compositions may also include fillers, added to theelastomeric (or other) composition to adjust the density and/or specificgravity of the center. Non-limiting examples of fillers include zincoxide, barium sulfate, and regrind, e.g., recycled core molding matrixground to about 30 mesh particle size. The amount and type of fillerutilized is governed by the amount and weight of other ingredients inthe composition, bearing in mind a maximum golf ball weight of 1.620 ozhas been established by the USGA. Fillers usually range in specificgravity from about 2.0 to about 5.6. The amount of filler in the centermay be lower such that the specific gravity of the center is decreased.

The specific gravity of the center may range, for example, from about0.8 to about 1.3, depending upon such factors as the size of the center,cover, intermediate layer and finished ball, as well as the specificgravity of the cover and intermediate layer. Other components such asaccelerators, e.g., tetra methylthiuram, processing aids, processingoils, plasticizers, dyes and pigments, antioxidants, as well as otheradditives well known to the skilled artisan may also be used in amountssufficient to achieve the purpose for which they are typically used.

Intermediate Layer(s)

The golf ball also may have one or more intermediate layers formed, forexample, from dynamically vulcanized thermoplastic elastomers,functionalized styrene-butadiene elastomers, thermoplastic rubbers,polybutadiene rubbers, natural rubbers, thermoset elastomers,thermoplastic urethanes, metallocene polymers, thermoset urethanes,ionomer resins, or blends thereof. For example, an intermediate layermay include a thermoplastic or thermoset polyurethane. Non-limiting ofcommercially available dynamically vulcanized thermoplastic elastomersinclude SANTOPRENE®, SARLINK®, VYRAM®, DYTRON®, and VISTAFLEX®.SANTOPRENE® is a dynamically vulcanized PP/EPDM. Examples offunctionalized styrene-butadiene elastomers, i.e., styrene-butadieneelastomers with functional groups such as maleic anhydride or sulfonicacid, include KRATON FG-1901x and FG-1921x, which are available from theShell Corporation of Houston, Tex.

Examples of suitable thermoplastic polyurethanes include ESTANE® 58133,ESTANE® 58134 and ESTANE® 58144, which are commercially available fromthe Lubrizol of Cleveland, Ohio.

Examples of metallocene polymers, i.e., polymers formed with ametallocene catalyst, include those commercially available from SentinelProducts of Hyannis, Mass. Suitable thermoplastic polyesters includepolybutylene terephthalate. Thermoplastic ionomer resins may be obtainedby providing a cross metallic bond to polymers of monoolefin with atleast one member selected from the group consisting of unsaturated mono-or di-carboxylic acids having 3 to 12 carbon atoms and esters thereof(the polymer contains 1 to 50 percent by weight of the unsaturated mono-or di-carboxylic acid and/or ester thereof). More particularly, lowmodulus ionomers such as acid-containing ethylene copolymer ionomers,include E/X/Y copolymers where E is ethylene, X is a softening comonomersuch as acrylate or methacrylate. Non-limiting examples of ionomerresins include SURLYN® and IOTEK®, which are commercially available fromDuPont and Exxon, respectively.

Alternatively, the intermediate layer(s) may be a blend of a first and asecond component wherein the first component is a dynamically vulcanizedthermoplastic elastomer, a functionalized styrene-butadiene elastomer, athermoplastic or thermoset polyurethane or a metallocene polymer and thesecond component is a material such as a thermoplastic or thermosetpolyurethane, a thermoplastic polyetherester or polyetheramide, athermoplastic ionomer resin, a thermoplastic polyester, anotherdynamically vulcanized elastomer, another a functionalizedstyrene-butadiene elastomer, another a metallocene polymer or blendsthereof. At least one of the first and second components may include athermoplastic or thermoset polyurethane.

One or more intermediate layers also may be formed from a blendcontaining an ethylene methacrylic/acrylic acid copolymer. Non-limitingexamples of acid-containing ethylene copolymers include ethylene/acrylicacid; ethylene/methacrylic acid; ethylene/acrylic acid/n- or isobutylacrylate; ethylene/methacrylic acid/n- or iso-butyl acrylate;ethylene/acrylic acid/methyl acrylate; ethylene/methacrylic acid/methylacrylate; ethylene/acrylic acid/iso-bornyl acrylate or methacrylate andethylene/methacrylic acid/isobornyl acrylate or methacrylate. Examplesof commercially available ethylene methacrylic/acrylic acid copolymersinclude NUCREL® polymers, available from DuPont.

Alternatively, the intermediate layer(s) may be formed from a blendwhich includes an ethylene methacrylic/acrylic acid copolymer and asecond component which includes a thermoplastic material. Suitablethermoplastic materials for use in the intermediate blend include, butare not limited to, polyesterester block copolymers, polyetheresterblock copolymers, polyetheramide block copolymers, ionomer resins,dynamically vulcanized thermoplastic elastomers, styrene-butadieneelastomers with functional groups such as maleic anhydride or sulfonicacid attached, thermoplastic polyurethanes, thermoplastic polyesters,metallocene polymers, and/or blends thereof.

An intermediate layer often, has a specific gravity of about 0.8 ormore. In some examples the intermediate layer has a specific gravitygreater than 1.0, e.g., ranging from about 1.02 to about 1.3. Specificgravity of the intermediate layer may be adjusted, for example, byadding a filler such as barium sulfate, zinc oxide, titanium dioxide andcombinations thereof.

The intermediate layer blend may have a flexural modulus of less thanabout 15,000 psi, often from about 5,000 to about 8,000 psi. Theintermediate layers often have a Shore D hardness of about 35 to 70. Theintermediate layer and core construction together may have a compressionof less than about 65, often from about 50 to about 65. Usually, theintermediate layer has a thickness from about 0.020 inches to about 0.2inches. The golf balls may include a single intermediate layer or aplurality of intermediate layers. In the case where a ball includes aplurality of intermediate layers, a first intermediate layer outside thecore may include, for example, a thermoplastic material or a rubbermaterial (synthetic or natural) having a hardness greater than that ofthe core.

A second intermediate layer may be disposed around the firstintermediate layer and may have a greater hardness than that of thefirst intermediate layer. The second intermediate layer may be formed ofmaterials such as polyether or polyester thermoplastic urethanes,thermoset urethanes, and ionomers such as acid-containing ethylenecopolymer ionomers.

In addition, if desired, a third intermediate layer (or even morelayers) may be disposed in between the first and second intermediatelayers. The third intermediate layer may be formed of the variety ofmaterials as discussed above. For example, the third intermediate layermay have a hardness greater than that of the first intermediate layer.

The Cover Layer

A golf ball also typically has a cover layer that includes one or morelayers of a thermoplastic or thermosetting material. A variety ofmaterials may be used such as ionomer resins, thermoplasticpolyurethanes, balata and blends thereof.

The cover may be formed of a composition including very low modulusionomers (VLMIs). As used herein, the term “very low modulus ionomers,”or the acronym “VLMIs,” are those ionomer resins further including asoftening comonomer X, commonly a (meth)acrylate ester, present fromabout 10 weight percent to about 50 weight percent in the polymer. VLMIsare copolymers of an α-olefin, such as ethylene, a softening agent, suchas n-butyl-acrylate or iso-butyl-acrylate, and an α, β-unsaturatedcarboxylic acid, such as acrylic or methacrylic acid, where at leastpart of the acid groups are neutralized by a magnesium cation. Otherexamples of softening comonomers include n-butyl methacrylate, methylacrylate, and methyl methacrylate. Generally, a VLMI has a flexuralmodulus from about 2,000 psi to about 10,000 psi. VLMIs are sometimesreferred to as “soft” ionomers.

Ionomers, such as acid-containing ethylene copolymer ionomers, includeE/X/Y copolymers where E is ethylene, X is a softening comonomer such asacrylate or methacrylate present in 0 to 50 weight percent of thepolymer, and Y is acrylic or methacrylic acid present in 5 to 35 (often10 to 20) weight percent of the polymer, wherein the acid moiety isneutralized 1 to 90 percent (usually at least 40 percent) to form anionomer by a cation such as lithium, sodium, potassium, magnesium,calcium, barium, lead, tin, zinc or aluminum, or a combination of suchcations, lithium, sodium and zinc being the most preferred. Specificacid-containing ethylene copolymers include ethylene/acrylic acid,ethylene/methacrylic acid, ethylene/acrylic acid/n-butyl acrylate,ethylene/methacrylic acid/n-butyl acrylate, ethylene/methacrylicacid/iso-butyl acrylate, ethylene/acrylic acid/iso-butyl acrylate,ethylene/methacrylic acid/n-butyl methacrylate, ethylene/acrylicacid/methyl methacrylate, ethylene/acrylic acid/methyl acrylate,ethylene/methacrylic acid/methyl acrylate, ethylene/methacrylicacid/methyl methacrylate, and ethylene/acrylic acid/n-butylmethacrylate.

To aid in the processing of the cover stock, ionomer resins may beblended in order to obtain a cover having desired characteristics. Forthis reason, the cover may be formed from a blend of two or more ionomerresins. The blend may include, for example, a very soft material and aharder material. Ionomer resins with different melt flow indexes areoften employed to obtain the desired characteristics of the cover stock.SURLYN® 8118, 7930 and 7940 have melt flow indices of about 1.4, 1.8,and 2.6 g/10 min., respectively. SURLYN® 8269 and SURLYN® 8265 each havea melt flow index of about 0.9 g/10 min. A blend of ionomer resins maybe used to form a cover having a melt flow index, for example, of fromabout 1 to about 3 g/10 min. The cover layer may have a Shore Dhardness, for example, ranging from about 45 to about 80.

The cover also may include thermoplastic and/or thermoset materials. Forexample, the cover may include a thermoplastic material such as urethaneor polyurethane. Polyurethane is a product of a reaction between apolyurethane prepolymer and a curing agent. The polyurethane prepolymeris a product formed by a reaction between a polyol and a diisocyanate.Often, a catalyst is employed to promote the reaction between the curingagent and the polyurethane prepolymer. In the case of castpolyurethanes, the curing agent is typically either a diamine or glycol.

As another example, a thermoset cast polyurethane may be used. Thermosetcast polyurethanes are generally prepared using a diisocyanate, such as2,4-toluene diisocyanate (TDI), methylenebis-(4-cyclohexyl isocyanate)(HMDI), or para-phenylene diisocyanate (“PPDI”) and a polyol which iscured with a polyamine, such as methylenedianiline (MDA), or atrifunctional glycol, such as trimethylol propane, or tetrafunctionalglycol, such as N,N,N′,N′-tetrakis(2-hydroxpropyl)ethylenediamine. Othersuitable thermoset materials include, but are not limited to, thermoseturethane ionomers and thermoset urethane epoxies. Other examples ofthermoset materials include polybutadiene, natural rubber, polyisoprene,styrene-butadiene, and styrene-propylene-diene rubber.

When the cover includes more than one layer, e.g., an inner cover layerand an outer cover layer, various constructions and materials aresuitable. For example, an inner cover layer may surround theintermediate layer with an outer cover layer disposed thereon or aninner cover layer may surround a plurality of intermediate layers. Whenusing an inner and outer cover layer construction, the outer cover layermaterial may be a thermoset material that includes at least one of acastable reactive liquid material and reaction products thereof, asdescribed above, and may have a hardness from about 30 Shore D to about60 Shore D.

The inner cover layer may be formed from a wide variety of hard (e.g.,about 50 Shore D or greater), high flexural modulus resilient materials,which are compatible with the other materials used in the adjacentlayers of the golf ball. The inner cover layer material may have aflexural modulus of about 65,000 psi or greater. Suitable inner coverlayer materials include the hard, high flexural modulus ionomer resinsand blends thereof, which may be obtained by providing a cross metallicbond to polymers of monoolefin with at least one member selected fromthe group consisting of unsaturated mono- or di-carboxylic acids having3 to 12 carbon atoms and esters thereof (the polymer contains 1 to 50percent by weight of the unsaturated mono- or di-carboxylic acid and/orester thereof). More particularly, such acid-containing ethylenecopolymer ionomer component includes E/X/Y copolymers where E isethylene, X is a softening comonomer such as acrylate or methacrylatepresent in 0-50 weight percent of the polymer, and Y is acrylic ormethacrylic acid present in 5-35 weight percent of the polymer, whereinthe acid moiety is neutralized about 1-90 percent to form an ionomer bya cation such as lithium, sodium, potassium, magnesium, calcium, barium,lead, tin, zinc, or aluminum, or a combination of such cations. Specificexamples of acid-containing ethylene copolymers include ethylene/acrylicacid, ethylene/methacrylic acid, ethylene/acrylic acid/n-butyl acrylate,ethylene/methacrylic acid/n-butyl acrylate, ethylene/methacrylicacid/iso-butyl acrylate, ethylene/acrylic acid/iso-butyl acrylate,ethylene/methacrylic acid/n-butyl methacrylate, ethylene/acrylicacid/methyl methacrylate, ethylene/acrylic acid/methyl acrylate,ethylene/methacrylic acid/methyl acrylate, ethylene/methacrylicacid/methyl methacrylate, and ethylene/acrylic acid/n-butylmethacrylate.

Examples of other suitable inner cover materials include thermoplasticor thermoset polyurethanes, polyetheresters, polyetheramides, orpolyesters, dynamically vulcanized elastomers, functionalizedstyrene-butadiene elastomers, metallocene polymers, polyamides such asnylons, acrylonitrile butadiene-styrene copolymers (ABS), or blendsthereof.

Manufacturing Process

While golf balls in accordance with examples of this invention may bemade in any desired manner without departing from this invention,including in conventional manners as are known and used in the art, onecommon technique for manufacturing golf balls is a laminate process. Inorder to form multiple layers around the center, a laminate is firstformed. The laminate includes at least two layers and sometimes includesthree layers. The laminate may be formed by mixing uncured core materialto be used for each layer and calendar rolling the material into thinsheets. Alternatively, the laminate may be formed by mixing uncuredintermediate layer material and rolling the material into sheets. Thelaminate sheets may be stacked together to form a laminate having threelayers, using calender rolling mills. Alternatively, the sheets may beformed by extrusion.

A laminate also may be formed using an adhesive between each layer ofmaterial. For example, an epoxy resin may be used as adhesive. Theadhesive should have good shear and tensile strength, for example, atensile strength over about 1500 psi. The adhesive often has a Shore Dhardness of less than about 60 when cured. The adhesive layer applied tothe sheets should be very thin, e.g., less than about 0.004 inchesthick.

Preferably, each laminate sheet is formed to a thickness that isslightly larger than the thickness of the layers in the finished golfball. Each of these thicknesses can be varied, but all have a thicknessof preferably less than about 0.1 inches. The sheets should have veryuniform thicknesses.

The next step in the method is to form multiple layers around thecenter. This may be accomplished by placing two laminates between a topmold and a bottom mold. The laminates may be formed to the cavities inthe mold halves. The laminates then may be cut into patterns that, whenjoined, form a laminated layer around the center. For example, thelaminates may be cut into figure 8-shaped or barbell-like patterns,similar to a baseball or a tennis ball cover. Other patterns may beused, such as curved triangles, hemispherical cups, ovals, or otherpatterns that may be joined together to form a laminated layer aroundthe center. The patterns may then be placed between molds and formed tothe cavities in the mold halves. A vacuum source often is used to formthe laminates to the mold cavities so that uniformity in layer thicknessis maintained.

After the laminates have been formed to the cavities, the centers arethen inserted between the laminates. The laminates are then compressionmolded about the center under conditions of temperature and pressurethat are well known in the art. The mold halves usually have vents toallow flowing of excess layer material from the laminates during thecompression molding process. As an alternative to compression molding,the core and/or intermediate layer(s) may be formed by injection moldingor other suitable technique.

The next step involves forming a cover around the golf ball core. Thecore, including the center and any intermediate layers, may be supportedwithin a pair of cover mold-halves by a plurality of retractable pins.The retractable pins may be actuated by conventional means known tothose of ordinary skill in the art.

After the mold halves are closed together with the pins supporting thecore, the cover material is injected into the mold in a liquid statethrough a plurality of injection ports or gates, such as edge gates orsub-gates. With edge gates, the resultant golf balls are allinterconnected and may be removed from the mold halves together in alarge matrix. Sub-gating automatically separates the mold runner fromthe golf balls during the ejection of the golf balls from mold halves.

The retractable pins may be retracted after a predetermined amount ofcover material has been injected into the mold halves to substantiallysurround the core. The liquid cover material is allowed to flow andsubstantially fill the cavity between the core and the mold halves,while maintaining concentricity between the core and the mold halves.The cover material is then allowed to solidify around the core, and thegolf balls are ejected from the mold halves and subjected to finishingprocesses, including coating, painting, and/or other finishingprocesses, including processes in accordance with examples of thisinvention, as will be described in more detail below.

B. General Description of the Ionomer/Hydrophobic TPU Layer

The Ionomer/hydrophobic TPU layer comprises a blend of at least oneionomer and hydrophobic thermoplastic polyurethane (hydrophobic TPU).The blend is applied to a golf ball in any suitable manner such as witha molding process step.

The ionomer/hydrophobic TPU layer may be part of the cover layer, forexample, an inner layer of the cover layer, or may be one of theintermediate or inner layers between the core and the cover layer.

C. Aspects of Invention

An aspect of this invention relate to golf balls having anionomer/hydrophobic TPU inner layer positioned between the core layerand the cover layer. The ionomer/hydrophobic TPU layer comprises a blendof at least one ionomer and hydrophobic thermoplastic polyurethane. Inone aspect the ionomer/hydrophobic TPU layer is an inner layer adjacentthe cover layer. In another aspect the ionomer/hydrophobic TPU layer isan inner layer adjacent the core.

Another aspect of this invention relate to golf balls having a covercomprising at least one layer comprising a blend of at least one ionomerand hydrophobic thermoplastic polyurethane.

Given the general description of various example aspects of theinvention provided above, more detailed descriptions of various specificexamples of golf ball structures according to the invention are providedbelow.

D. Detailed Description of Example Golf Balls, and Methods According toAspects of the Invention

The following discussion and accompanying figures describe variousexample golf balls in accordance with aspects of the present invention.

Aspects of the invention utilize an ionomer/hydrophobic TPU layercomprising a blend of ionomer and hydrophobic thermoplastic polyurethane(hydrophobic TPU). The ionomer/hydrophobic TPU layer has a Shore Dhardness suitable for golf balls but also provides effective moistureprotection to the golf ball.

In particular, the ionomer and hydrophobic TPU blend provides a moisturebarrier layer having a Water Vapor Transmission Rate (WVTR) of less than1300 in grams/m² after 168 hrs at 25° C. and 50% relative humidity forinstance of less than 1000, preferably less than 750.

The Shore D hardness of an ionomer/TPU cover layer or inner layer isbetween 20 and 85. “Shore D hardness” refers to a measure of thehardness of a material by a durometer, and especially the material'sresistance to indentation. Shore D hardness may be measured with adurometer directly on the curved surface of the core, layer, cover,etc., according to ASTM method D2240. In other embodiments, the hardnessmay be measured using standard plaques. An alternative scale to Shore Dis Shore A hardness. Shore A hardness is generally between 60 and 99 ormore.

The specific gravity of the ionomer/TPU layer is generally greater than0.80 and less than 1.0. The specific gravity of the composite of layersof a golf ball should be sufficiently high enough to approach but notexceed the USGA limit of 1.620 oz. in order to have a USGA conformingball. “Specific gravity (SG)” refers to the conventional meaning of theratio of the density of a given solid (or liquid) to the density ofwater at a specific temperature and pressure.

Hydrophobic TPU is described in US Publication 20090192262 and is asemicrystalline, thermoplastic polyurethane which is comprised of thereaction product of (1) a hydrophobic polyol, (2) a polyisocyanate, and(3) a linear chain extender containing 5 carbon atoms or 7 to 12 carbonatoms; wherein the hydrophobic polyol has a number average molecularweight which is within the range of about 1,000 to about 4,000; whereinthe semicrystalline, thermoplastic polyurethane has a weight averagemolecular weight which is within the range of 50,000 to 1,000,000; andwherein the semicrystalline, thermoplastic polyurethane has a meltingpoint which is within the range of 80° C. to 150° C. US Publication20090192262 is hereby incorporated by reference in its entirety.

The hydrophobic polyol can be a diol of a conjugated diolefin monomer, apolyisobutylene diol, a polyester polyol prepared from fatty diolsand/or fatty diacids, or mixtures thereof. For instance, the hydrophobicpolyol can be prepared from dimer fatty alcohols and/or dimer fattyacids. The diols of conjugated olefin monomers that can be used includehydrogenated polybutadienediols, and hydrogenated polyisoprene diol.Hydrogenated polybutadiene polyols are sold by Mitsubishi ChemicalCorporation under the trade name POLYTAIL and Kraton polyols sold byKraton Polymers of Houston, Tex.

Dimeric acid polyester polyols may contain from about 18 to about 44carbon atoms Dimer acids (and esters thereof) are a well knowncommercially available class of dicarboxylic acids (or esters). Thedimer acid material will usually contain 26 to 44 carbon atoms.Particularly, examples include dimer acids (or esters) derived from C₁₈and C₂₂ unsaturated monocarboxylic acids (or esters) which will yield,respectively, C₃₆ and C₄₄ dimer acids (or esters). Dimer acids derivedfrom C₁₈ unsaturated acids, which include acids such as linoleic andlinolenic are particularly well known (yielding C₃₆ dimer acids). Thedimer acid products will normally also contain a proportion of trimeracids (C₅₄ acids when using C₁₈ starting acids), possibly even higheroligomers and also small amounts of the monomer acids. Several differentgrades of dimer acids are available from commercial sources and thesediffer from each other primarily in the amount of monobasic and trimeracid fractions and the degree of unsaturation. Priplast™ polyesterpolyols are branched C₃₆ dimerized fatty acids which are particularlyuseful as the hydrophobic polyol. Priplast™ polyester polyols arecommercially available from Uniqema of Gouda, Netherlands. Thehydrophobic polyol used in synthesizing the hydrophobic TPU willtypically have a number average molecular weight which is within therange of about 1,500 to about 4,000 and a number average molecularweight which is within the range of about 2,000 to about 3,000.

The linear chain extender used in making the hydrophobic TPU willtypically be of the structural formula:

wherein n represents the integer 5 or an integer from 7 to 12.Accordingly, the linear chain extender may be selected from the groupconsisting of 1,5-pentane diol, 1,7-heptane diol, 1,8-octane diol,1,9-nonane diol, 1,10-decane diol, 1,11-undecane diol, 1,12-dodecanediol, and mixtures thereof.

The polyisocyanate may be a diisocyanate such as aliphatic diisocyanatesand aromatic diisocyanates. Multifunctional isocyanate compounds, i.e.,triisocyanates, etc., which cause crosslinking, are generally avoidedand thus the amount used, if any, is generally less than 4 mole percentand preferably less than 2 mole percent based upon the total moles ofall of the various isocyanates used. Suitable diisocyanates includearomatic diisocyanates such as: 4,4′-methylene bis-(phenyl isocyanate)(MDI); m-xylene diisocyanate (XDI), phenylene-1-4-diisocyanate,naphthalene-1,5-diisocyanate,diphenylmethane-3,3′-dimethoxy-4,4′-diisocyanate, and toluenediisocyanate (TDI); as well as aliphatic diisocyanates such asisophorone diisocyanate (IPDI), 1,4-cyclohexyl diisocyanate (CHDI),decane-1,10-diisocyanate, and dicyclohexylmethane-4,4′-diisocyanate.Dimers and trimers of the above diisocyanates may also be used as wellas a blend of two or more diisocyanates may be used.

The polyisocyanate may be in the form of a low molecular weight polymeror oligomer which is end capped with an isocyanate. For example, thehydroxyl terminated polyether intermediate described above may bereacted with an isocyanate-containing compound to create a low molecularweight polymer end capped with isocyanate. In the TPU art, suchmaterials are normally referred to as pre-polymers. Such pre-polymersnormally have a number average molecular weight (Mn) which is within therange of about 500 to about 10,000.

The mole ratio of the one or more diisocyanates is generally from about0.95 to about 1.05, or from about 0.98 to about 1.03 moles per mole ofthe total moles of the one or more hydrophobic polyols and the one ormore chain extenders. The molar ratio of the chain extender to thepolyol will typically be within the range of about 0.3:1 to 10:1 andwill more typically be within the range of about 0.4:1 to 5:1. The molarratio of the chain extender to the polyol may be within the range ofabout 0:5:1 to 3:1 or the range of about 0.5:1 to 2:1.

US Publication 20090192262 further describes various processes of makingthe hydrophobic TPU. Any suitable method is acceptable for the presentapplication.

Catalysts such as stannous and other metal carboxylates as well astertiary amines may be used to prepare the hydrophobic TPU. Examples ofmetal carboxylates catalysts include stannous octoate, dibutyl tindilaurate, phenyl mercuric propionate, lead octoate, ironacetylacetonate, magnesium acetylacetonate, and the like. Examples oftertiary amine catalysts include triethylene diamine, and the like. Theamount of the one or more catalysts is generally from about 50 to about100 parts by weight per million parts by weight of the end TPU polymerformed.

The weight average molecular weight (Mw) of the hydrophobic TPU polymerrange from about 50,000 to about 500,000 Daltons, from about 100,000 toabout 500,000 Daltons, and from about 120,000 to about 300,000 Daltons.The Mw of the TPU polymer is measured according to gel permeationchromatography (GPC) against polystyrene standard.

When a higher molecular weight hydrophobic TPU polymer is desired, itcan be achieved by using a small amount of a cross linking agent havingan average functionality greater than 2.0 to induce cross linking. Theamount of cross linking agent used is less than 2 mole percent of thetotal moles of chain extender, or less than 1 mole percent. Less than 1mole percent of the chain extender may be replaced with trimethylolpropane (TMP). The cross linking is accomplished by adding a crosslinking agent having an average functionality greater than 2.0 togetherwith the hydrophobic polyol, the isocyanate compound, and chain extenderin the reaction mixture to manufacture the TPU polymer. The amount ofcross linking agent used in the reaction mixture to make the TPU polymerwill depend on the desired molecular weight and the effectiveness of theparticular cross linking agent used. Usually, less than 2.0 molepercent, or less than 1.0 mole percent, based on the total moles ofchain extender used in making the TPU polymer are used. The level ofcross linking agent used is generally from about 0.05 mole percent toabout 2.0 mole percent based on the total moles of chain extender.

The cross linking agents can be any monomeric or oligomeric materialswhich have an average functionality of greater than 2.0 and have theability to cross link the TPU polymer. Such materials are well known inthe art of thermoset polyurethanes such as trimethylol propane (TMP) andpentaerythritol.

The hydrophobic TPU has a melting point which is within the range ofabout 80° C. to about 150° C. It will typically have a melting pointwhich is within the range of about 90° C. to about 145° C., and willmore typically have a melting point which is within the range of about110° C. to about 140° C.

Hydrophobic TPU is much more effective as a moisture barrier thanordinary TPU. However, hydrophobic TPU is a very soft material, 60-70 A,which is very soft for a golf ball. TPUs are segmented polymers havingsoft segments and hard segments. This feature accounts for theirexcellent elastic properties. The soft segments are derived from thehydroxyl terminated polyether or polyester and the hard segments arederived from the isocyanate and the chain extender. The chain extenderis typically one of a variety of glycols, such as 1,4-butane glycol.

Ionomers, such as acid-containing ethylene copolymer ionomers, includeE/X/Y copolymers where E is ethylene, X is a softening comonomer such asacrylate or methacrylate present in 0 to 50 weight percent of thepolymer, and Y is acrylic or methacrylic acid present in 5 to 35 (often10 to 20) weight percent of the polymer, wherein the acid moiety isneutralized 1 to 90 percent (usually at least 40 percent) to form anionomer by a cation such as lithium, sodium, potassium, magnesium,calcium, barium, lead, tin, zinc or aluminum, or a combination of suchcations, lithium, sodium and zinc being the most preferred. Specificacid-containing ethylene copolymers include ethylene/acrylic acid,ethylene/methacrylic acid, ethylene/acrylic acid/n-butyl acrylate,ethylene/methacrylic acid/n-butyl acrylate, ethylene/methacrylicacid/iso-butyl acrylate, ethylene/acrylic acid/iso-butyl acrylate,ethylene/methacrylic acid/n-butyl methacrylate, ethylene/acrylicacid/methyl methacrylate, ethylene/acrylic acid/methyl acrylate,ethylene/methacrylic acid/methyl acrylate, ethylene/methacrylicacid/methyl methacrylate, and ethylene/acrylic acid/n-butylmethacrylate.

The ionomer may include a blend of two or more ionomer resins. The blendmay include, for example, a very soft material and a harder material.Ionomer resins with different melt flow indexes are often employed toobtain the desired characteristics of the cover stock. SURLYN® 8118,7930 and 7940 have melt flow indices of about 1.4, 1.8, and 2.6 g/10min., respectively. SURLYN® 8269 and SURLYN® 8265 each have a melt flowindex of about 0.9 g/10 min. A blend of ionomer resins may be used toform a cover having a melt flow index, for example, of from about 1 toabout 3 g/10 min. The cover layer may have a Shore D hardness, forexample, ranging from about 45 to about 80.

In accordance with aspects of the invention, the hydrophobic TPU isblended with one or more ionomers to make a “hardness-suitable” butstill moisture resistant layer cover layer. For example, the blend mayprovide a softer cover to add wedge-spin performance of a typicalionomer covered ball and improve scruff resistance.

In accordance with other aspects of the invention, the hydrophobic TPUis blended with one or more ionomers to add softness or flexibility aswell as moisture-resistant properties to inner layers such as mantle orcore layers.

The amount of the ionomer is from about 5 percent to about 95 percent byweight based upon the total weight of the ionomer and hydrophobic TPUblend, 15 percent to about 85 percent, and also between 20 percent andabout 80 percent, or between 30 percent and 70 percent. The amount ofthe hydrophobic TPU is from about 95 percent by weight to about 5percent by weight based upon the total weight of the Ionomer andhydrophobic TPU blend, 15 percent to about 85 percent, and also between20 percent and about 80 percent, or between 30 percent and 70 percent.

The hydrophobic TPU and ionomer are mixed or blended in a suitablemanner. The mixing can utilize conventional melt processing techniquesand can either be batch or continuous such as through the use of asingle or a twin screw extruder. The mixing temperature is generallyabove the melting point of the ionomer, and the hydrophobic TPU. Suchtemperatures are generally from about 180° C. to about 240° C. Themixing time will naturally vary depending upon the amount of componentsbeing blended together, the mixing equipment used, and the mixingtemperature.

Additional additives optionally may be incorporated into the ionomer/TPUblend, such as flow additives, mar/slip additives, adhesion promoters,thickeners, gloss reducers, flexibilizers, cross-linking additives,isocyanates or other agents for toughening or creating scratchresistance, optical brighteners, UV absorbers, and the like. The amountof such additives usually ranges from 0 to about 20 wt %, often from 0to about 6 wt %.

The hydrophobic TPU and Ionomer blend is applied to a golf ball with onemolding process step, for example. The method of applying the resin isnot limited.

The thickness of the applied blend (after drying, curing, cooling,hardening, or setting) typically ranges from of about 0.5 to about 5.0mm, and in some examples, from about 0.75 to about 3.0 mm.

The golf ball body of the present invention has no limitation on itsstructure and includes a one-piece golf ball, a two-piece golf ball, amulti-piece golf ball comprising at least three layers, and a wound-coregolf ball. The present invention can be applied for all types of thegolf ball.

Example

The tables below display 6 different blends and their correspondingMoisture Vapor Transmission Rates (WVTR). FIG. 4 displays the trend invapor transmission as the % hydrophobic TPU (H-TPU) is increased from 0%to 5% to 10%. It is desirable to keep shore A hardness below 90 A tomaintain good wedge abrasion. Blend 6 has the lowest transmission but istoo hard.

Blends:

Existing Cover Blend Reduced WVTR Blends Estane Blend # grade 1 2 3 4 56 58219 75% 50% 40% 63% 60% 58280 25% 50% 60% 32% 30% 25% H-TPU 0% 0% 0%5% 10% 0% ETE 50DT3 75%

Performance:

Blend # 1 2 3 4 5 6 Shore A 86 85 84 87 86 92 Hardness, 5 sec ASTM D2240Moisture vapor 930 1100 1500 1200 1000 650 transmission, Upright Cup 25C., 50% RH 5 mil film Loss, g/m2 after 168 hrs

CONCLUSION

The present invention is described above and in the accompanyingdrawings with reference to a variety of example structures, features,elements, and combinations of structures, features, and elements. Thepurpose served by the disclosure, however, is to provide examples of thevarious features and concepts related to the invention, not to limit thescope of the invention. One skilled in the relevant art will recognizethat numerous variations and modifications may be made to theembodiments described above without departing from the scope of thepresent invention, as defined by the appended claims. For example, thevarious features and concepts described above in conjunction with thefigures may be used individually and/or in any combination orsubcombination without departing from this invention.

1. A golf ball, comprising at least one layer comprising a blend ofionomer and hydrophobic thermoplastic polyurethane.
 2. The golf ball ofclaim 1 wherein the hydrophobic thermoplastic polyurethane comprises thereaction product of (1) a hydrophobic polyol, (2) a polyisocyanate, and(3) a linear chain extender containing 5 carbon atoms or 7 to 12 carbonatoms; wherein the hydrophobic polyol has a number average molecularweight which is within the range of about 1,000 to about 4,000; whereinthe semicrystalline, thermoplastic polyurethane has a weight averagemolecular weight which is within the range of 50,000 to 1,000,000; andwherein the semicrystalline, thermoplastic polyurethane has a meltingpoint which is within the range of 80° C. to 150° C.
 3. The golf ball ofclaim 1 wherein the at least one layer has a Water Vapor TransmissionRate (WVTR) of less than 1300 g/m2 after 168 hrs at 25 C and 50%relative humidity.
 4. The golf ball of claim 1 wherein the at least onelayer has a Water Vapor Transmission Rate (WVTR) of less than 1000 g/m2after 168 hrs at 25 C and 50% relative humidity.
 5. The golf ball ofclaim 1 wherein the at least one layer has a Shore D hardness is between20 and
 85. 6. The golf ball of claim 1 wherein the at least one layerhas a specific gravity of greater than 0.80 and less than 1.00.
 7. Thegolf ball of claim 1 wherein the ionomer is an acid-containing ethylenecopolymer ionomer.
 8. The golf ball of claim 7 wherein theacid-containing ethylene copolymer ionomer is selected from the groupconsisting of ethylene/acrylic acid, ethylene/methacrylic acid,ethylene/acrylic acid/n-butyl acrylate, ethylene/methacrylicacid/n-butyl acrylate, ethylene/methacrylic acid/iso-butyl acrylate,ethylene/acrylic acid/iso-butyl acrylate, ethylene/methacrylicacid/n-butyl methacrylate, ethylene/acrylic acid/methyl methacrylate,ethylene/acrylic acid/methyl acrylate, ethylene/methacrylic acid/methylacrylate, ethylene/methacrylic acid/methyl methacrylate, andethylene/acrylic acid/n-butyl methacrylate.
 9. The golf ball of claim 1wherein the ionomer is a blend of ionomers.
 10. The golf ball of claim 1wherein the at least one layer comprises from about 5 percent to about95 percent by weight ionomer based upon the total weight of the ionomerand hydrophobic thermoplastic polyurethane blend and from about 95percent by weight to about 5 percent by weight hydrophobic thermoplasticpolyurethane based upon the total weight of the ionomer and hydrophobicthermoplastic polyurethane blend.
 11. The golf ball of claim 1 whereinthe at least one layer comprises from about 15 percent to about 85percent by weight ionomer based upon the total weight of the ionomer andhydrophobic thermoplastic polyurethane blend and from about 15 percentby weight to about 85 percent by weight hydrophobic thermoplasticpolyurethane based upon the total weight of the ionomer and hydrophobicthermoplastic polyurethane blend.
 12. A golf ball, comprising: a core;and a cover comprising a moisture barrier layer and an outer layer;wherein the moisture barrier layer comprises a blend of ionomer andhydrophobic thermoplastic polyurethane.
 13. The golf ball of claim 12wherein the hydrophobic thermoplastic polyurethane comprises thereaction product of (1) a hydrophobic polyol, (2) a polyisocyanate, and(3) a linear chain extender containing 5 carbon atoms or 7 to 12 carbonatoms; wherein the hydrophobic polyol has a number average molecularweight which is within the range of about 1,000 to about 4,000; whereinthe semicrystalline, thermoplastic polyurethane has a weight averagemolecular weight which is within the range of 50,000 to 1,000,000; andwherein the semicrystalline, thermoplastic polyurethane has a meltingpoint which is within the range of 80° C. to 150° C.
 14. The golf ballof claim 12 wherein the moisture barrier layer has a Water VaporTransmission Rate (WVTR) of less than 1300 g/m2 after 168 hrs at 25 Cand 50% relative humidity.
 15. The golf ball of claim 12 wherein themoisture barrier layer has a Water Vapor Transmission Rate (WVTR) ofless than 1000 g/m2 after 168 hrs at 25 C and 50% relative humidity. 16.The golf ball of claim 12 wherein the moisture barrier layer has a ShoreD hardness is between 20 and
 85. 17. The golf ball of claim 12 whereinthe moisture barrier layer has a specific gravity of greater than 0.80and less than 1.00.
 18. The golf ball of claim 12 wherein the ionomer isan acid-containing ethylene copolymer ionomer.
 19. The golf ball ofclaim 18 wherein the acid-containing ethylene copolymer ionomer isselected from the group consisting of ethylene/acrylic acid,ethylene/methacrylic acid, ethylene/acrylic acid/n-butyl acrylate,ethylene/methacrylic acid/n-butyl acrylate, ethylene/methacrylicacid/iso-butyl acrylate, ethylene/acrylic acid/iso-butyl acrylate,ethylene/methacrylic acid/n-butyl methacrylate, ethylene/acrylicacid/methyl methacrylate, ethylene/acrylic acid/methyl acrylate,ethylene/methacrylic acid/methyl acrylate, ethylene/methacrylicacid/methyl methacrylate, and ethylene/acrylic acid/n-butylmethacrylate.
 20. The golf ball of claim 12 wherein the ionomer is ablend of ionomers.
 21. The golf ball of claim 12 wherein the moisturebarrier layer comprises from about 5 percent to about 95 percent byweight ionomer based upon the total weight of the ionomer andhydrophobic thermoplastic polyurethane blend and from about 95 percentby weight to about 5 percent by weight hydrophobic thermoplasticpolyurethane based upon the total weight of the ionomer and hydrophobicthermoplastic polyurethane blend.
 22. The golf ball of claim 12 whereinthe moisture barrier layer comprises from about 15 percent to about 85percent by weight ionomer based upon the total weight of the ionomer andhydrophobic thermoplastic polyurethane blend and from about 15 percentby weight to about 85 percent by weight hydrophobic thermoplasticpolyurethane based upon the total weight of the ionomer and hydrophobicthermoplastic polyurethane blend.
 23. A method of improving moistureresistance of a golf ball comprising applying a moisture barrier layerto a golf ball, the moisture barrier layer comprising a blend of ionomerand hydrophobic thermoplastic polyurethane.